Sarlink TPV 3170 - High temperature resistance, high wear resistance
Price:30
Other Products
Description
Additional Information
Sarlink TPV 3170 - High Temperature Resistance, High Wear Resistance Sarlink? 3100 Series: General Purpose TPV These general purpose TPVs exhibit balanced flow characteristics, resulting in excellent surface appearance. The Sarlink? series offers a range from 35 Shore A to 45 Shore D (black and natural colors), partially cross-linked, with outstanding melt elasticity, processable by injection or blow molding and extrusion.
| Sarlink TPV 3170 - High Temperature Resistance, High Wear Resistance Molding Method | Injection MoldingExtrusion | |||
Sarlink TPV 3170 - High Temperature Resistance, High Wear Resistance Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 0.94 g/cm3 | ASTM D792 | |
Shrinkage | |||
Longitudinal (Flow) | 1.8 % | Internal | 3mm thickness |
Transverse (Across Flow) | 1.4 % | Internal | 3mm thickness |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
At 100% Elongation | 3.1 MPa | ASTM D 412 | Cross direction |
At 100% Elongation | 3.6 MPa | ASTM D 412 | Flow direction |
- | 7.7 MPa | ASTM D 412 | Cross direction |
- | 5.2 MPa | ASTM D 412 | Flow direction |
Elongation at Break | |||
Break (brk) | 683 % | ASTM D 412 | Cross direction |
Break (brk) | 378 % | ASTM D 412 | Flow direction |
Tear Strength | 42 kN/m | ASTM D 624 | Unnicked, Cross direction |
Compression Set | 47 % | ASTM D 395 | 125℃, 70Hrs |
Compression Set | 25 % | ASTM D 395 | 23℃, 22Hrs |
Compression Set | 43 % | ASTM D 395 | 70℃, 22Hrs |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Brittleness Temperature | -65 °C | ISO 812 | |
| Hardness Properties | Value/Unit | Test Standard | Test Conditions |
Shore Hardness A | 71 A | ASTM D 2240 | 5sec, Extruded sample |
Shore Hardness A | 73 A | ASTM D 2240 | 5sec, Injection molded sample |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | - mm | UL94 | |
| Aging Properties | Value/Unit | Test Standard | Test Conditions |
Hardness (Thermal Aging) | 2 - | ASTM D573 | Change, 135℃, 1000Hrs |
Hardness (Thermal Aging) | 3 - | ASTM D573 | Change, 150℃, 168Hrs |
Tensile Strength (Thermal Aging) | 92 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Tensile Strength (Thermal Aging) | 96 % | ASTM D573 | Retention, 150℃, 168Hrs |
Elongation (Thermal Aging) | 86 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Elongation (Thermal Aging) | 86 % | ASTM D573 | Retention, 150℃, 168Hrs |
Volume Change | 114 % | ASTM D471 | ASTM Oil#3, 125℃, 70Hrs |
| Industry Category: | Rubber & Plastics/Thermoplastic Elastomers/TPV (Thermoplastic Vulcanizate) |
|---|---|