TPV 3150 - Thermoplastic Vulcanizate Elastomer
Price:30
Other Products
Description
Additional Information
TPV 3150 - Vulcanized Rubber Elastomer Thermoplastic Vulcanizate (TPV) is the preferred solution for critical applications requiring excellent elasticity and long-term performance. With faster and more economical processing, TPV 3150 - Vulcanized Rubber Elastomer offers a sustainable alternative to thermoset rubber in sealing applications. The Sarlink portfolio* has recently expanded to include styrenic TPEs, introducing unique performance characteristics such as improved flow properties for more complex designs. While our competitors focus on one chemistry, at Teknor Apex we offer multiple chemistries under one brand, enabling us to recommend the most suitable solution for your specific application.
| TPV 3150 - Vulcanized Rubber Elastomer Molding Method | Injection MoldingExtrusion | |||
TPV 3150 - Vulcanized Rubber Elastomer Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 0.94 g/cm3 | ASTM D792 | |
Shrinkage | |||
Longitudinal (Flow) | 2.5 % | Internal | 3mm thickness |
Transverse (Across Flow) | 1.5 % | Internal | 3mm thickness |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
At 100% Elongation | 1.8 MPa | ASTM D 412 | Cross direction |
At 100% Elongation | 2.2 MPa | ASTM D 412 | Flow direction |
- | 4.7 MPa | ASTM D 412 | Cross direction |
- | 3.3 MPa | ASTM D 412 | Flow direction |
Tensile Elongation | |||
At Break (brk) | 581 % | ASTM D 412 | Cross direction |
At Break (brk) | 316 % | ASTM D 412 | Flow direction |
Tear Strength | 24 kN/m | ASTM D 624 | Unnicked, Cross direction |
Compression Set | 41 % | ASTM D 395 | 125℃, 70Hrs |
Compression Set | 20 % | ASTM D 395 | 23℃, 22Hrs |
Compression Set | 37 % | ASTM D 395 | 70℃, 22Hrs |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Brittleness Temperature | -65 °C | ISO 812 | |
| Hardness Properties | Value/Unit | Test Standard | Test Conditions |
Shore Hardness A | 54 A | ASTM D 2240 | 5sec, Extruded sample |
Shore Hardness A | 57 A | ASTM D 2240 | 5sec, Injection molded sample |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | - mm | UL94 | |
| Aging Properties | Value/Unit | Test Standard | Test Conditions |
Hardness (Thermal Aging) | 6 - | ASTM D573 | Change, 135℃, 1000Hrs |
Hardness (Thermal Aging) | 4 - | ASTM D573 | Change, 150℃, 168Hrs |
Tensile Strength (Thermal Aging) | 96 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Tensile Strength (Thermal Aging) | 94 % | ASTM D573 | Retention, 150℃, 168Hrs |
Elongation (Thermal Aging) | 94 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Elongation (Thermal Aging) | 79 % | ASTM D573 | Retention, 150℃, 168Hrs |
Volume Change | 117 % | ASTM D471 | ASTM Oil# |