Sarlink TPV 3180 - Vulcanized Rubber Polymer
Price:30
Other Products
Description
Additional Information
Colette Polymer (Shenzhen) Co., Ltd. Long-term sales of Sarlink TPV 3180 - Vulcanized Rubber Polymer, ample supply, regular stock;
Sarlink TPVs
Excellent elastic properties
UV and ozone resistance
Chemical and fluid resistance
Outstanding long-term performance
Adhesion to polyolefins and other TPEs
3100 Series: General Purpose TPV
Sarlink 3135, 3139D, 3140, 3145D, 3150, 3160, 3160-43, 3170, 3175-01, 3180, 3190
Sarlink 3380N-02, 3439D, 3440, 3445D, 3450, 3460, 3470, 3480, 3490
Sarlink 3745D, 3760, 3770, 3780, 3790, 3790-40, 3939D-01, 3939DN,
| Sarlink TPV 3180 - Vulcanized Rubber Polymer Molding Method | Injection MoldingExtrusion | |||
Sarlink TPV 3180 - Vulcanized Rubber Polymer Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 0.95 g/cm3 | ASTM D792 | |
Shrinkage | |||
Longitudinal (Flow) | 1.8 % | Internal | 3mm thickness |
Transverse (Across Flow) | 1.3 % | Internal | 3mm thickness |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
At 100% Elongation | 4.5 MPa | ASTM D 412 | Cross direction |
At 100% Elongation | 5.1 MPa | ASTM D 412 | Flow direction |
- | 9.3 MPa | ASTM D 412 | Cross direction |
- | 7.1 MPa | ASTM D 412 | Flow direction |
Tensile Elongation | |||
At Break (brk) | 676 % | ASTM D 412 | Cross direction |
At Break (brk) | 430 % | ASTM D 412 | Flow direction |
Tear Strength | 51 kN/m | ASTM D 624 | Unnicked, Cross direction |
Compression Set | 52 % | ASTM D 395 | 125℃, 70Hrs |
Compression Set | 32 % | ASTM D 395 | 23℃, 22Hrs |
Compression Set | 46 % | ASTM D 395 | 70℃, 22Hrs |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Brittleness Temperature | -59 °C | ISO 812 | |
| Hardness Properties | Value/Unit | Test Standard | Test Conditions |
Shore Hardness A | 80 A | ASTM D 2240 | 5sec, Extruded sample |
Shore Hardness A | 83 A | ASTM D 2240 | 5sec, Injection molded sample |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | - mm | UL94 | |
| Aging Properties | Value/Unit | Test Standard | Test Conditions |
Hardness (Heat Aging) | 0 - | ASTM D573 | Change, 135℃, 1000Hrs |
Hardness (Heat Aging) | 2 - | ASTM D573 | Change, 150℃, 168Hrs |
Tensile Strength (Heat Aging) | 128 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Tensile Strength (Heat Aging) | 92 % | ASTM D573 | Retention, 150℃, 168Hrs |
Elongation (Heat Aging) | 143 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Elongation (Heat Aging) | 84 % | ASTM D573 | Retention, 150℃, 168Hrs |
Volume Change | 95 % | ASTM D471 | ASTM Oil# |
| Industry Category: | Rubber & Plastics/Thermoplastic Elastomers/TPV (Thermoplastic Vulcanizate) |
|---|---|