TPV 3140 - Injection Molding, Extrusion Applications
Price:30
Other Products
Description
Additional Information
| TPV 3140 - Injection Molding, Extrusion Applications Molding Method | Injection MoldingExtrusion | |||
Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Conditions |
|---|---|---|---|
Density | 0.93 g/cm3 | ASTM D792 | |
Shrinkage | |||
Longitudinal (Flow) | 2.8 % | Internal | 3mm thickness |
Transverse (Across Flow) | 1.6 % | Internal | 3mm thickness |
| Mechanical Properties | Value/Unit | Test Standard | Test Conditions |
Tensile Strength | |||
At 100% Elongation | 1 MPa | ASTM D 412 | Cross direction |
At 100% Elongation | 1.3 MPa | ASTM D 412 | Flow direction |
- | 3.8 MPa | ASTM D 412 | Cross direction |
- | 2.6 MPa | ASTM D 412 | Flow direction |
Tensile Elongation | |||
Break (brk) | 552 % | ASTM D 412 | Cross direction |
Break (brk) | 328 % | ASTM D 412 | Flow direction |
Tear Strength | 16 kN/m | ASTM D 624 | Unnicked, Cross direction |
Compression Set | 42 % | ASTM D 395 | 125℃, 70Hrs |
Compression Set | 32 % | ASTM D 395 | 23℃, 22Hrs |
Compression Set | 34 % | ASTM D 395 | 70℃, 22Hrs |
| Impact Properties | Value/Unit | Test Standard | Test Conditions |
Brittleness Temperature | -63 °C | ISO 812 | |
| Hardness Properties | Value/Unit | Test Standard | Test Conditions |
Shore Hardness A | 40 A | ASTM D 2240 | 5sec, Extruded sample |
Shore Hardness A | 46 A | ASTM D 2240 | 5sec, Injection molded sample |
| Flammability Properties | Value/Unit | Test Standard | Test Conditions |
UL Flame Rating | |||
HB | - mm | UL94 | |
| Aging Properties | Value/Unit | Test Standard | Test Conditions |
Hardness (Thermal Aging) | 3 - | ASTM D573 | Change, 135℃, 1000Hrs |
Hardness (Thermal Aging) | 1 - | ASTM D573 | Change, 150℃, 168Hrs |
Tensile Strength (Thermal Aging) | 103 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Tensile Strength (Thermal Aging) | 111 % | ASTM D573 | Retention, 150℃, 168Hrs |
Elongation (Thermal Aging) | 110 % | ASTM D573 | Retention, 135℃, 1000Hrs |
Elongation (Thermal Aging) | 107 % | ASTM D573 | Retention, 150℃, 168Hrs |
Volume Change | 133 % | ASTM D471 | ASTM Oil# |
| Industry Category: | Rubber & Plastics/Thermoplastic Elastomers/TPV (Thermoplastic Vulcanizate) |
|---|---|