National Standard Epoxy Zinc-Rich Primer is supplied to various regions including Sichuan, Chengdu, Yunnan, etc.; Manager Sun 152_0825_6966; Kogran Coatings (Guan Brand) is a zinc-rich primer that can be used as an anti-corrosion coating for metal surfaces. It has excellent corrosion resistance, capable of withstanding harsh environments such as oxidation, chemical corrosion, and marine corrosion. 20+2 kg, available in medium gray, light gray, and dark gray.

This product is an epoxy zinc-rich heavy-duty anti-corrosion primer, primarily formulated with epoxy resin as the main film-forming base, supplemented with modified resins, special additives, auxiliaries, solvents, etc., prepared through a specific process.

Suitable for use as an anti-rust primer for indoor or outdoor exposed steel surfaces, as well as for bridges, ships, offshore platforms, underwater coatings, harbor facilities, automotive chassis metal surface rust prevention, and internal/external wall rust prevention primer for oil tanks; it can also serve as a chemical anti-corrosion coating, conductive paint, cathodic protection, and anti-corrosion coating for coal mine facilities.

Main Features:

1. Excellent coating performance. The coating offers outstanding adhesion, weather resistance, and water resistance, with superior rust prevention, acid resistance, oil resistance, solvent resistance, impact strength, flexibility, durability, and abrasion resistance.

2. Easy to use, cures at room temperature. Compatible with topcoats.

Application Reference

1. Recommended film thickness: 60-80 μm.

2. The surface to be coated must be free of scale, rust, oil, and other contaminants.

3. Usage: 0.2-0.25 kg per square meter (excluding loss).

4. Mixed paint must be used within 6 hours.

5. Applicable by brushing, air spraying, or rolling.

6. Continuous stirring is required during application to prevent settling.

7. Substrate temperature must be at least 3°C above the dew point. When the substrate temperature is below 5°C, the film will not cure, so application is not recommended.

8. After opening Component A, it must be stirred thoroughly. Then, while stirring, pour Component B into Component A according to the specified ratio, mix evenly, let stand, mature for 30 minutes, add an appropriate amount of thinner, and adjust to the application viscosity.

Some article content is excerpted from the internet. If there is any discomfort, please contact us to inform, and we will handle it as soon as possible. Thank you.