Sales of Guan Brand and Keshushi Floor Paint (supply to Sichuan, Chengdu, Yunnan, etc.) Consultation on room-temperature self-drying floor coatings (Manager Sun 152~0825~6966). Koguan floor paint offers advantages such as wear resistance, pressure resistance, chemical corrosion resistance, aesthetic appeal, and easy cleaning, making it widely applicable in industrial floors, warehouses, parking lots, and other venues.

Guan Brand Epoxy Floor Paint Construction Method/Steps:

1. Try to avoid construction during high-temperature periods; staggered construction during morning and evening hours is recommended. Before using any materials, fully stir Component B, then pour Components A and B into the mixing bucket in proportion and mix thoroughly. After maturation, add quartz powder or other powder materials, stir uniformly, and then use.

2. In summer high temperatures, surface coating may exhibit slight color separation, with possible occurrences of gray or blue shades. Ensure thorough stirring before use.

3. When summer temperatures are excessively high, use the mixed materials as soon as possible, typically within 30 minutes, to prevent material solidification.

4. Epoxy floor manufacturers adopt manual cooling measures to reduce the construction environment temperature.

5. To manage the relative humidity of the construction environment, manual humidification of the construction site can be employed.

6. After construction by the epoxy floor paint manufacturer, ensure dedicated personnel are present on-site to monitor, preventing dry shrinkage cracks in the epoxy floor due to excessive temperatures.

Product Technical Indicators:

Item Indicator

Color Appearance Various colors

Condition in Container Uniform after stirring, no hard lumps

Drying Time (h) Surface Dry ≤2

Hard Dry ≤48

Pencil Hardness ≥H

Adhesion (Cross-Cut Method, grade) ≤1

Impact Resistance (cm) 50

Abrasion Resistance (750g/500r, weight loss, g) ≤0.06

Flexibility/mm ≤2

Water Resistance (7d) No blistering, no peeling, slight discoloration allowed

Alkali Resistance (10% NaOH, 48h) No blistering, no peeling, slight discoloration allowed