Ceramic fiber board
Contact Info
- Add:青浦區(qū)紀(jì)鶴公路6626號(hào), Zip:
- Contact: 文海龍
- Tel:13761670937
- Email:hhwhl@126.com
Other Products
Product Description
Huoya ceramic fiber boards are manufactured using high-purity ceramic fibers as the primary raw material, with the addition of inorganic and a small amount of organic binders. They are produced using specialized vacuum forming equipment. The temperature resistance grades include: 1000°C, 1260°C, 1400°C, 1500°C, 1600°C, 1700°C, and 1800°C. Due to the inclusion of organic binders during production, initial use may result in smoke and a burnt odor, which is normal. Customers should operate the boards under working conditions for 24 hours to eliminate these effects. The company can produce inorganic boards, hardened boards, hydrophobic boards, and vitrified boards according to customer requirements.
Product Characteristics
Smooth board surface
Uniform density and thickness
Excellent mechanical and structural strength
Resistance to airflow erosion
Low thermal conductivity, low shrinkage, low density
Exceptional high-temperature resistance
Product Applications
Insulation and thermal barrier layers for various industrial furnace hot faces
Ultra-high temperature, rapid heating, and cooling test furnaces
Ceramic and electronic industry roller hearth kilns, shuttle kilns, tunnel kilns, pusher plate kilns, sintering furnaces
Glass industry annealing furnaces, tempering furnaces, bending furnaces
Mechanical and metallurgical industry heat treatment furnaces, heating furnaces, forging furnaces
Chemical industry cracking furnaces, reforming furnaces, hydrogen production furnaces, atmospheric and vacuum distillation furnaces, coking furnaces
Hot face and backing insulation for other thermal equipment
Physical and Chemical Indicators
Model | 1000 Fiber Board | 1260 Fiber Board | 1400 Fiber Board | 1600 Fiber Board | 1800 Fiber Board |
Classification Temperature (°C) | 1000 | 1260 | 1400 | 1600 | 1800 |
Density (Kg/m3) | 250-350 | 250-350 | 250-350 | 300-350 | 300-500 |
Heating Linear Shrinkage (%) (°C*24 hours) | 1.3 (900) | 1.1 (1100) | 1.6 (1200) | 1.2 (1400) | 1.0 (1600) |
Flexural Strength (kg/cm2) | 5 | 5 | 5 | 6 | 6 |
Slag Ball Content (>212 μm) (%) | 8 | 8 | 8 | 8 | 8 |
Thermal Conductivity Kcal/mh°C (W/mK), ASTM C201 | |||||
250 kg/m3 | 250 kg/m3 | 250 kg/m3 | 300 kg/m3 | 350 kg/m3 | |
Average 400°C | 0.08 | 0.09 | |||
Average 600°C | 0.13 | 0.14 | 0.1 | 0.12 | |
Average 800°C | 0.2 | 0.18 | 0.14 | 0.16 | |
Average 1000°C | 0.2 | <極端>0.211 | |||
Average 1200°C | 0.232 | ||||
Chemical Composition | |||||
Al?O? | 38 | 42 | 50 | 68 | 85 |
SiO? + Al?O? | 96 | 98 | 99 | 99.5 | 99.8 |
Fe?O? | 0.2 | 0.2 | 0.2 | ~ | ~ |
Standard Dimensions (mm/piece) | 1200*1200*25 / 50; | ||||
1000*600*6 / 12.5 / 20 / 25 / 30 / 40 / 50 | |||||
Product Standard Specifications
1000×600×3-100mm, 1000×1200×10-100mm
900×600×6-100mm, 900×1200×10-100mm
1100×700×10-100mm
| Industry Category | Metallurgy & Minerals/Powder Metallurgy/Other Powder Metallurgy |
|---|---|
| Product Category | |
| Brand: | 火雅熱能 |
| Spec: | 1000*1200*50 |
| Stock: | 1000 |
| Manufacturer: | |
| Origin: | China / Shanghai / Qingpuqu |