The W-B92 Webster
Hardness Tester is calibrated using
HRB standard Rockwell hardness blocks, with a measurement range equivalent to 48-100HRB. This hardness range covers almost all common soft steel materials. Comparative tests show that the measured values of the W-B92 hardness tester have an approximate linear relationship with HRB Rockwell hardness values, as shown in the figure below. The W-B92 hardness tester can be used as a convenient HRB Rockwell hardness tester.Applications
＊ Inspect the effectiveness of material heat treatment to determine if the mechanical properties meet standards.
＊ Determine if the material has been improperly alloy processed.
＊ Differentiate material hardness grades. Identify material heat treatment states such as annealed, 1/8 hard, 1/4 hard, 1/2 hard, and full hard.
＊ Online inspection and control of strip steel material hardness.
Technical Specifications
Range: 0-20HW
Accuracy: 0.5HW
Weight: 0.5kg
Measurement Range: Equivalent to Rockwell Hardness 48-100HRB
Vickers Hardness 90-253HV
Brinell Hardness 85.5-241HB
Tensile Strength 285-810MPa/mm2
Sample Dimensions: Sheet Thickness: 0.4mm-6mm
Pipe Thickness: 0.3mm-6mm
Pipe Inner Diameter: Ø10mm and above
Hardness Blocks
The standard hardness blocks used with the instrument are made of aluminum alloy or low carbon steel, with a hardness value of approximately 55HRB Rockwell hardness. Each hardness block comes with an inspection report.
Conversion
Users can determine the conversion relationship between Webster hardness values and Vickers hardness values (HV) or Rockwell hardness values (HRB) through testing.
Standard Configuration
Main Unit 1 unit
Standard Hardness Block 1 block
Spare Indenter 1 piece
Calibration Wrench 1 piece
Small Screwdriver 1 piece
Instrument Case 1 unit
Optional Accessories
Standard Hardness Block (Low Carbon Steel and Aluminum Alloy, with Inspection Report)
Spare Indenter
Dial Glass