A002 Stainless Steel Welding Electrode
GB/T 983 E308L-16 AWS A5.4 E308L-16 ISO 3581-A-E (19 9 L) R 3 2 ISO 3581-B-ES 308L-16
Suitable for welding 022Cr19Ni10 and 06Cr18Ni11Ti stainless steel structures, primarily used in the manufacturing of synthetic fiber, fertilizer, petroleum, and other equipment.
An ultra-low carbon Cr19Ni10 stainless steel electrode with a rutile-type coating, offering excellent welding process performance, good resistance to porosity, resistance to coating reddening and cracking, and superior resistance to intergranular corrosion.
AC, DC reverse polarity (AC, DC+), with DC reverse polarity recommended.
Deposited Metal Chemical Composition (%)
| Test Item | C | Mn | Si | P | S | Cr | Ni | Mo | Cu |
| GB/T Standard | ≤0.04 | 0.50～2.50 | ≤1.00 | ≤0.040 | ≤0.030 | 18.0～21.0 | 9.0～12.0 | ≤0.75 | ≤0.75 |
| Example Value | 0.024 | 1.30 | 0.62 | 0.020 | 0.008 | 19.90 | 9.80 | 0.040 | 0.035 |
Deposited Metal Mechanical Properties
| Test Item | Rm (MPa) | A(%) |
| GB/T Standard | ≥510 | ≥30 |
| Example Value | 580 | 45 |
Reference Current
| Electrode Diameter (mm) | Φ2.5 | Φ3.2 | Φ4.0 | Φ5.0 | |
| Welding Current (A) | Flat, Horizontal | 50～90 | 80～120 | 100～150 | 140～180 |
| Vertical, Overhead | 60～80 | 90～110 | 110～140 | — | |
1. Drying Requirement: Electrodes must be baked at 300°C for 1 hour before use and used immediately after baking.
2. When using AC welding, spatter is higher, the coating is prone to reddening, and penetration is shallower; therefore, DC reverse polarity welding is recommended.
3. Use low current and short arc welding as much as possible during welding, with minimal oscillation amplitude.
| Industry Category | Hardware & Tools/Welding Materials & Accessories/Other Welding Materials |
|---|---|
| Product Category | |
| Brand: | 金帝牌 |
| Spec: | 2.5/3.2/4.0/5.0mm |
| Stock: | 8000 |
| Manufacturer: | |
| Origin: | China / Hebei / Xingtaishi |