Tungsten Carbide Wear-Resistant Hardfacing Electrode D707
Contact Info
- Add:河北省邢臺市信都區(qū)永康街533號, Zip:
- Contact: 韓吉英
- Tel:13833921539
- Email:2891465062@qq.com
Other Products
GB/T 984 EDW-A-15
Suitable for hardfacing mechanical parts subjected to severe rock abrasion, such as concrete mixer blades, bulldozer and pump blades, dredger blades, high-speed sand mixing boxes, etc.
A low-hydrogen sodium-type flux-coated CW hardfacing electrode. The hardfacing metal has a high tungsten content and exhibits high hardness.
Direct current reverse polarity (DC+)
Chemical Composition of Deposited Metal (%)
| Test Item | C | Mn | Si | W |
| GB/T Standard | 1.50–3.00 | ≤2.00 | ≤4.00 | 40.00–50.00 |
| Example Value | 2.38 | 1.92 | 1.52 | 42.50 |
Hardness of Hardfacing Metal
| Test Item | HRC (4 layers or more) |
| GB/T Standard | ≥60 |
Reference Current
| Electrode Size (mm) | Φ3.2 | Φ4.0 | Φ5.0 |
| Welding Current (A) | 90–130 | 120–170 | 160–210 |
1. Drying requirement: Electrodes must be baked at 300–350°C for 1 hour before use and used immediately after baking.
2. Preheating temperature for carbon steel hardfacing parts: above 300°C; for low-alloy steel hardfacing parts: 400–500°C; for stainless steel hardfacing parts: 600–650°C.
3. It is advisable to use a low current during welding.
4. Low-alloy steel and stainless steel parts must undergo annealing at 700°C after welding.
| Industry Category | |
|---|---|
| Product Category | |
| Brand: | 金帝牌 |
| Spec: | 2.5/3.2/4.0/5.0mm |
| Stock: | 5000 |
| Manufacturer: | |
| Origin: | China / Hebei / Xingtaishi |